| Titanium Grade
5 (6Al-4V) |
3.7165 |
| |
UNS R56400 |
Ti-6Al-4V alloy is the most widely used titanium alloy of the alpha-plus-beta class, and is also the most common of all titanium alloys. The alloy is castable and is utilized “as cast” in sporting goods. The wrought material is used in aerospace, medical, and other applications where moderate strength, good strength to weight, and favorable corrosion properties are required.
Stock program
| Bars: |
ASTM B 348, AMS 4928 |
| Sheet/Plates: : |
ASTM B 265, AMS 4911 |
| |
|
| Bars, cold or hot rolled, annealed, centerless ground or machined |
kg /
m |
| Ø |
5.00 mm |
|
|
|
0.087 |
| Ø |
8.00 mm |
|
|
|
0.223 |
| Ø |
10.00 mm |
|
|
|
0.348 |
| Ø |
12.00 mm |
|
|
|
0.501 |
| Ø |
16.00 mm |
|
|
|
0.891 |
| Ø |
18.00 mm |
|
|
|
1.127 |
| Ø |
20.00 mm |
|
|
|
1.392 |
| Ø |
25.00 mm |
|
|
|
2.175 |
| Ø |
30.00 mm |
|
|
|
3.131 |
| Ø |
35.00 mm |
|
|
|
4.262 |
| Ø |
40.00 mm |
|
|
|
5.567 |
| Ø |
45.00 mm |
|
|
|
7.046 |
| Ø |
50.00 mm |
|
|
|
8.698 |
| Ø |
55.00 mm |
|
|
|
10.525 |
| Ø |
60.00 mm |
|
|
|
12.526 |
| Ø |
65.00 mm |
|
|
|
14.700 |
| Ø |
70.00 mm |
|
|
|
17.049 |
| Ø |
80.00 mm |
|
|
|
22.268 |
| Ø |
90.00 mm |
|
|
|
28.183 |
| Ø |
100.00 mm |
|
|
|
34.793 |
| Ø |
120.00 mm |
|
|
|
50.102 |
| Ø |
125.00 mm |
|
|
|
54.364 |
| Ø |
130.00 mm |
|
|
|
58.801 |
| Ø |
140.00 mm |
|
|
|
68.195 |
| Ø |
150.00 mm |
|
|
|
78.285 |
| Ø |
160.00 mm |
|
|
|
89.071 |
| Ø |
180.00 mm |
|
|
|
112.730 |
| Ø |
200.00 mm |
|
|
|
139.173 |
| Ø |
250.00 mm |
|
|
|
|
| |
|
|
|
|
|
| Sheets & plates , cold or hot rolled annealed |
|
| |
available in the following thicknesses: |
|
|
| |
0.40 |
mm |
|
|
|
1.77 |
| |
0.50 |
mm |
|
|
|
2.22 |
| |
0.60 |
mm |
|
|
|
2.66 |
| |
0.80 |
mm |
|
|
|
3.54 |
| |
1.00 |
mm |
|
|
|
4.43 |
| |
1.20 |
mm |
|
|
|
5.32 |
| |
1.40 |
mm |
|
|
|
6.20 |
| |
1.60 |
mm |
|
|
|
7.09 |
| |
1.80 |
mm |
|
|
|
7.97 |
| |
2.00 |
mm |
|
|
|
8.86 |
| |
2.10 |
mm |
|
|
|
9.30 |
| |
2.30 |
mm |
|
|
|
10.19 |
| |
2.50 |
mm |
|
|
|
11.08 |
| |
3.18 |
mm |
|
|
|
14.09 |
| |
4.00 |
mm |
|
|
|
17.72 |
| |
4.76 |
mm |
|
|
|
21.09 |
| |
5.00 |
mm |
|
|
|
22.15 |
| |
6.00 |
mm |
|
|
|
26.58 |
| |
6.35 |
mm |
|
|
|
28.13 |
| |
8.00 |
mm |
|
|
|
35.44 |
| |
9.53 |
mm |
|
|
|
42.22 |
| |
10.00 |
mm |
|
|
|
44.30 |
| |
12.00 |
mm |
|
|
|
53.16 |
| |
12.70 |
mm |
|
|
|
56.26 |
| |
14.00 |
mm |
|
|
|
62.02 |
| |
15.00 |
mm |
|
|
|
66.45 |
| |
16.00 |
mm |
|
|
|
70.88 |
| |
19.05 |
mm |
|
|
|
84.39 |
| |
25.40 |
mm |
|
|
|
112.52 |
| |
|
|
|
|
|
| => Plates with thickness up to 200 mm are available ex works.
|
| |
|
|
|
|
|
|
| Limiting |
| Ti |
balance |
|
| Al |
5.50 - 6.75 |
% |
| V |
3.50 - 4.50 |
% |
| Fe |
max. |
0.40 |
% |
| O |
max. |
0.20 |
% |
| C |
max. |
0.08 |
% |
| N |
max. |
0.05 |
% |
| H |
max. |
0.015 |
% |
| Density |
| g/cm³ |
4.43 |
| lb/in³ |
0.160 |
|