A nickel-iron-chromium alloy with an addition of silicon. It has good high-temperature strength and excellent resistance to oxidation and
carburization. The silicon content makes the alloy resistant to internal oxidation in high-temperature atmospheres that vary between oxidizing and reducing. Used in industrial furnaces and for heat-treating baskets, trays,
and fixtures.
Stock program
| |
|
| Bars, cold drawn |
kg /
m |
| Ø |
8.00 mm |
|
0.40 |
| |
|
|
|
| Bars, hot finished, annealed |
kg /
m |
| Ø |
12.00 mm |
|
0.89 |
| Ø |
20.00 mm |
|
2.47 |
| Ø |
25.00 mm |
|
3.86 |
| Ø |
30.00 mm |
|
5.56 |
| Ø |
40.00 mm |
|
9.88 |
| Ø |
45.00 mm |
|
12.50 |
| Ø |
50.00 mm |
|
15.43 |
| Ø |
60.00 mm |
|
22.22 |
| Ø |
65.00 mm |
|
26.08 |
| Ø |
70.00 mm |
|
30.25 |
| Ø |
80.00 mm |
|
39.51 |
| Ø |
90.00 mm |
|
50.00 |
| Ø |
100.00 mm |
|
61.73 |
| |
|
|
|
| Sheets/Plates, hot rolled, annealed, descaled |
|
| 6.0 |
x 1500 x 3000 mm |
|
47.52 |
|
| Limiting |
| Ni¹ |
34.50
- 41.00 |
% |
| Fe |
balance |
|
| Cr |
17.00
- 19.00 |
% |
| Si |
1.90
- 2.60 |
% |
| Mn |
0.80 - 1.50 |
% |
| Cu |
max. |
0.50 |
% |
| Ti |
max. |
0.20 |
% |
| C |
max. |
0.10 |
% |
| S |
max. |
0.02 |
% |
| |
|
|
|
| ¹ Plus Co |
|
|
|
| Density |
| g/cm³ |
8.08 |
| lb/in³ |
0.292 |
| Recommended Welding Products |
| Electrode |
INCO WELD A |
| |
INCO WELD 117 |
| Filler Metal |
INCONEL 82 |
| |
INCONEL 617 |
|